Colore |
Au
% |
Pt
% |
Pd
% |
Ag
% |
Cu
% |
In
% |
Altri
% |
Dur.
Vickers
(HV 5)
fuso |
Dur.
Vickers
(HV 5)
temp |
Dur.
Vickers
(HV 5)
stemp |
Dur.
Vickers
(HV 5)
cotto |
Int. fusione °C |
Temp fusione °C |
Peso specif. gr/cm3 |
Coeff.
dilataz.
(um/mx)
25°-500°C |
Coeff.
dilataz.
(um/mx)
25°-600°C |
|
LEGHE PER CERAMICA |
|
Lite 52+ |
bianco |
15,0 |
- |
52,20 |
21,50 |
- |
6,00 |
5,30 |
240 |
|
290 |
|
1160-1290 |
1400 |
11,60 |
14,5 |
14,7 |
|
Lite 70+ |
bianco |
3,0 |
- |
70,0 |
9,5 |
|
2,0 |
15,50 |
260 |
|
|
|
1180-1290 |
1345 |
10,7 |
14,1 |
14,4 |
|
|
|
SALDATURE (per visualizzare la scheda di sicurezza, cliccare
sulla lega) |
|
P (1140) |
bianco |
23,0 |
- |
19,95 |
55,0 |
- |
- |
2,05 |
|
|
|
|
1110-1200 |
|
|
|
|
|
W (1100)
|
bianco
|
51,0
|
-
|
12,9
|
34,0
|
-
|
-
|
2,10
|
|
|
|
|
1095-1150
|
|
|
|
|
|
LO (710)
|
giallo
|
50,0
|
-
|
0,95
|
28,0
|
-
|
-
|
21,05
|
|
|
|
|
700-715
|
|
|
|
|
|
R (660) |
bianco |
- |
- |
2,25 |
52,0 |
24,0 |
- |
21,75 |
|
|
|
|
610-665 |
|
|
|
|
|
Leghe dentali
|
Colore |
Au
% |
Pt
% |
Pd
% |
Ag
% |
Cu
% |
In
% |
Altri
% |
Dur.
Vickers
(HV 5)
fuso |
Dur.
Vickers
(HV 5)
temp |
Dur.
Vickers
(HV 5)
stemp |
Dur.
Vickers
(HV 5)
cotto |
Int. fusione °C |
Temp fusione °C |
Peso specif. gr/cm3 |
Coeff.
dilataz.
(um/mx)
25°-500°C |
Coeff.
dilataz.
(um/mx)
25°-600°C |
|